COMBINATION OF IMPRESSED CURRENT AND SACRIFICIAL ANODE CATHODIC PREVENTION TO IMPROVE CORROSION PREVENTION SYSTEM IN REINFORCED CONCRETE

作成者
本文言語
出版者
発行日
収録物名
会議情報
出版タイプ
アクセス権
概要 In this study, effectiveness of impressed current cathodic prevention (ICCP) and sacrificial anode cathodic prevention (SACP) in corrosion prevention of rebar in reinforced concrete (RC) is compared. ...Firstly, SACP method is applied in chloride-contaminated specimens which are kept in air curing condition for 150 days, then changed to dry/wet cycle NaCl solution cycle condition. Result shows that extremely high initial protective current, then decreased drastically until being stabilized. The depolarization value increases in dry/wet cycle condition than air condition. Secondly, ICCP method is applied with different protective current density, where corrosion of the steel bars were accelerated beforehand. Result shows that higher current density provides higher depolarization value. However, even smaller current density still able to reach 100 mV criterion after 56 days of test period. Based on both results, ICCP and SACP were combined as “hybrid system” to extend the service life of SACP. Initial current consumption was controlled in ICCP stage before changing to SACP stage. Result shows that on potential value increases gradually in ICCP stage and stabilizes after changing to SACP stage, while depolarization value in SACP stage shows more stabilized value compared to the value in SACP only.続きを見る

本文ファイル

pdf 4481606 pdf 737 KB 715  

詳細

レコードID
主題
注記
登録日 2021.07.13
更新日 2021.07.13

この資料を見た人はこんな資料も見ています