Analysis of Small Spalling Mechanism on Hot Rolling Mill Roll Surface

作成者
本文言語
出版者
発行日
収録物名
開始ページ
終了ページ
出版タイプ
アクセス権
関連DOI
関連DOI
関連URI
関連URI
関連HDL
関連情報
概要 In order to analyze the small spalling mechanism on the surface of the hot rolling mill high speed steel roll, an actual hot rolling mill roll was investigated, and the thermal cycle and Mode II fatig...ue crack growth tests, which reflect the results of the investigation, were carried out. From the investigation of the actual hot rolling mill roll, it was proven that the small spalling was generated by heat crack initiation by thermal cycling and Mode II fatigue crack growth. The crack due to the thermal cycling was initiated in the oxide area. Estimation of the small spalling hot rolling mill roll life on the roll surface became possible based on the relationship between the crack growth rate da/dN and threshold Mode II stress intensity factor range $ΔK_IIth$, and it was clarified that the life of the Mode II fatigue crack growth was longer than that of the crack initiation life by thermal cycling.続きを見る

本文ファイル

pdf paper1 pdf 1.53 MB 247  

詳細

レコードID
査読有無
関連URI
主題
ISSN
NCID
タイプ
登録日 2009.04.22
更新日 2020.11.27

この資料を見た人はこんな資料も見ています