Fabrication and High Heat Flux Tests of Plasma Sprayed Tungsten Coated Carbon and TZM

作成者
本文言語
出版者
発行日
収録物名
開始ページ
終了ページ
出版タイプ
アクセス権
JaLC DOI
概要 High density tungsten is coated by vacuum plasma spraying technique (VPS) on tiles, 20mn x 20mn x 10mm. Substrate materials are carbon/carbon composite (CX-2002U), isotropic fine-grained graphite(IG-4...30U). Thickness of the tungsten-coating layer is 0.5 mm. The tungsten-coated tiles are jointed by Ti brazing on the OFHC surface with a cooling tube. In addition, VPS-W coated TZM also has been brazed. Thermal response and thermal fatigue lifetime tests using an electron beam facility have been carried out on the tungsten coated mock-ups under the active cooling condition. Heat flux is changed from 1 to 10 MW/m^2. The heat flux experiments have been carried out under the condition that the water flow velocity, pressure and temperature are 15.0 m/s, 0.5 MPa and 293 K, respectively. The use of high density VPS-W improves the performance of mock-ups under steady state heat flux condition. In addition, in the case of high density W coated CX-2002U on OFHC and W coated TZM on OFHC, it is demonstrated that the mock-up successfully withstood 100 cycles of heat loads at 10 MW/m^2 at steady state.続きを見る

本文ファイル

pdf 129_p097 pdf 8.20 MB 571  

詳細

PISSN
NCID
レコードID
査読有無
主題
タイプ
登録日 2013.08.09
更新日 2023.02.27

この資料を見た人はこんな資料も見ています