Surface characterisation and corrosion behaviour of oxide layer for SLMed-316L stainless steel

作成者
本文言語
出版者
発行日
収録物名
開始ページ
終了ページ
出版タイプ
アクセス権
関連DOI
概要 The stable oxide layer formed through thermal oxidation (TO) process on selective laser melted 316 L stainless steel (SLMed-316 L SS) substrate surface attested to assists in refining their corrosion ...resistance and observed to behave relatively inert in physiological conditions. The surface characterisation and corrosion behaviour of the oxidised SLMed-316 L SS are the primary focus of this study. The formation of the oxide layer on SLMed-316 L SS was investigated at constant ambient atmosphere and 700 °C temperature for three different soaking times (150, 200 and 250 h). The surface characterisation of the oxide layer was performed using Field Emission Scanning Electron Microscope (FESEM), Energy Dispersive X-ray Spectroscopy (EDX) and X-ray Diffraction (XRD) to correlate the thickness of oxide layer and surface morphology after the TO treatment. Whereas, the electrochemical analysis was conducted using potentiodynamic polarisation to investigate the corrosion behaviour of the oxide layer. The finding disclosed an increase in the oxide layer thickness formation at prolonged exposure in ambient atmosphere. Also, the TO at 150 h showed an improved corrosion behaviour due to the presence of Fe2O3 and Cr2O3 layers. However, the extended soaking time showed no improvement towards the corrosion behaviour.続きを見る

詳細

PISSN
EISSN
NCID
レコードID
権利関係
主題
登録日 2018.04.24
更新日 2018.05.09

この資料を見た人はこんな資料も見ています