PARTIALLY REPAIR METHOD OF DETERIORATED RC BEAMS BY SACRIFICIAL ANODE CATHODIC PROTECTION AND CORROSION INHIBITOR

作成者
本文言語
出版者
発行日
会議情報
出版タイプ
アクセス権
関連DOI
概要 Patch repair of deteriorating concrete, which mainly involves the replacement of chloride-contaminated concrete with the fresh alkaline patch concrete is a common intervention to rehabilitate the defe...cting reinforced concrete (RC) structure while the concrete replacement of this process is expensive. Application of curative corrosion inhibitor directly on the surface of corroding rebar before new patch material casting is recommended as easy to use approach for new corrosion attack. Sacrificial anodes have been used to limit the extension of concrete replacement and extend the service life of patch repair to RC member. This study focuses on the utilization of sacrificial anode cathodic protection arrangement and corrosion inhibitor in partially repair RC beams. Two specimens of 44-years of serious chloride-induced corrosion condition having a length of 2400 mm and 200x300 mm cross-section were prepared as RC-1 and RC-2. The polymer-modified mortar as the patch repair material was applied to the middle tension area in the dimension of 70x150x800mm. Four cylindrical ribbed sacrificial zinc anodes with 30 mm diameter and 130 mm length installed in the parent concrete by LiOH cementitious coating material. A specially modified epoxy paint as corrosion inhibitor was applied to the tensile steel bar surface of the patch repair section in RC-2. The exposure condition of the specimens was on two-days wet and followed by five-days dry in laboratory air condition until 12-months observation. Depolarization test of rebar by the calomel-saturated electrode (CSE) on the side section of specimen’s surface, the current density of sacrificial zinc anodes and rebar, anodic-cathodic polarization curve are measured regularly until 12-months observation as the performance evaluation was presented in this paper. The sacrificial zinc anode tested in this research affects polarizing the potential of rebar in the deteriorated RC member. However, the high polarization is limited to 15 cm away from anodes in parent concrete, not in the patch repair section, due to the inherent differences in the properties of patch repair material and parent concrete. The application of corrosion inhibitor in the rebar surface of patch repair part may extend the polarization effect of anodes and significantly increase the polarization distance until two times.続きを見る

本文ファイル

pdf 4483188 pdf 929 KB 188  

詳細

レコードID
関連URI
主題
登録日 2021.07.29
更新日 2021.07.29

この資料を見た人はこんな資料も見ています