<学術雑誌論文>
HA/ZrO_2 Coating on CoCr Alloy Using Flame Thermal Spray

作成者
本文言語
出版者
発行日
収録物名
開始ページ
終了ページ
出版タイプ
アクセス権
Crossref DOI
権利関係
概要 CoCr alloy is mostly used as biomaterial implant. However, it still has several weaknesses. Therefore, it is necessary to modify the surface to improve its biocompability. This research is a prelimina...ry study on CoCr coated with Hydroxyapatite (HA)/Zirconium Dioxide (ZrO_2) using Thermal Flame Spray method. 5 % - 20 % ZrO_2 was mixed with HA. Besides improving the biocompatibility, ZrO_2 is believed to be able to enhance the antibacterial properties. Characterization test was performed using FE-SEM. The coating was analyzed for corrosion rate, surface roughness and antibacterial activity. Adding ZrO_2 to HA has been proven to be able to improve corrosion rate. Combination of 80HA-20ZrO_2 is the most effective bioceramic mixture, producing lowest corrosion rate of 0.213 mm/year in HBSS media. This is due to the increased reactivity value and better passivation reaction than CoCr without coating. Antibacterial activity test revealed that the coating could form inhibitory area around the sample meaning that the coating can provide bacterial resistance for the implant.続きを見る

本文ファイル

pdf 254-261 pdf 1.48 MB 517  

詳細

PISSN
EISSN
レコードID
査読有無
主題
登録日 2022.07.01
更新日 2024.02.21

この資料を見た人はこんな資料も見ています